Low carbon steel draw wires

1. General Purpose low carbon content steel round wires according to the polish standard PN-67/M-80026 and wires for nail production

Diameter

(mm)

Weight

(kg)

Coil interior 

diameter (mm)

 Resistance to stretching Rm min (MPa) 

 0.50 - 0.75  20 - 30 140 - 160 -
0.80 - 1.30  30 - 100 160 - 250 750
1.40 - 1.80  80 - 150 250 - 350 700
1.90 - 2.20  100 - 150 300 - 400 700
2.30 - 2.70  100 - 250 350 - 450 650
2.80 - 3.70  200 - 300 350 - 500 600
3.80 - 4.60  200 - 300 450 - 550 550
4.70 - 8.00  200 - 300 450 - 650 550
9.00 - 12.00  200 - 300 600 - 700 550

Types of wires:

  • low tensile strenght (mild) wires Rm below - Rm <420 Mpa,
  • lower tensile strenght (semi - hard) wires - Rm 420 - 600 Mpa,
  • normal tensile strenght (hard) wires - Rm >600 MPa

Condition of wire surface:

  • grey bare - dry drawn - between 1.0 to 12.0 mm,
  • polished bare - wet drawn,
  • dark annealed bare - between 1.0 to 5.0 mm,
  • light annealed bare - between 0.2 to 1.2 mm,
  • wires under the shell plating

Packaging:

  • cardboard sleeves type Z2 - diameters range 1,0 - 1,2 mm,
  • metal racks - diameters range 2,0 - 4,5 mm,
  • reels combo - diameters range 2,3 - 9,0  mm, wire weight about 1000 kg

2. Square stranded cross - section wires

Diameter (mm) Weight (kg) Coil interior diameter (mm) 
 2.40 - 4.20  150 - 250  550 - 600

3. Black annealed wire for hops

4. Polished wire for home appliances industry

4. Special wires for bonderisation (individual orders)